| C | Mn | Si | P | S | Cr |
| 0.15 | 1.25 | 1.00 | 0.06 | 0.15 | 12.0-14.0 |
| Tempering Temperature (°C) | Tensile Strength (MPa) |
Yield Strength 0.2% Proof (MPa) |
Elongation (% in 50mm) |
Hardness Brinell (HB) |
Impact Charpy V (J) |
| Annealed * | 517 | 276 | 30 | 262 | – |
| Condition T ** | 758 | 586 | 18 | 248-302 | – |
| 204 | 1340 | 1050 | 11 | 388 | 20 |
| 316 | 1350 | 1060 | 12 | 388 | 22 |
| 427 | 1405 | 1110 | 11 | 401 | # |
| 538 | 1000 | 795 | 13 | 321 | # |
| 593 | 840 | 705 | 19 | 248 | 27 |
| 650 | 750 | 575 | 20 | 223 | 38 |
| * Annealed properties are typical for Condition A of ASTM A582. | |||||
| ** Hardened and tempered Condition T of ASTM A582 – Brinell Hardness is specified range, other properties are typical only. | |||||
| # Due to associated low impact resistance this steel should not be tempered in the range 400- | |||||
|
Density kg /m3 |
Thermal Conductivity W/mK |
Electrical Resistivity (Microhm/cm) |
Modulus of Elasticity |
Coefficient of Thermal Expansion µm/m/°C |
Specific Heat (J/kg.K) |
Specific Gravity |
| 7750 | 24.9at 212°F | 43 at 68°F | 200 GPa | 9.9 at 32 – 212°F | 460 at 32°F to 212°F | 7.7 |
Alloy 416 is a martensitic, free-machining, chromium steel alloy that is generally considered to be the first free-machining stainless steel. It has the highest machinability of any stainless steel at about 85% of that of a free-machining carbon steel. Martensitic stainless steels were designed to be hardenable by heat treatment and also corrosion resistant.
Although Alloy 416 and other martensitic stainless steels are not as resistant as austenitic or ferritic stainless, it still demonstrates good corrosion and oxidation resistance plus high strength in the hardened and tempered condition. Alloy 416HT is easily machined, is always magnetic, and has low frictional properties that reduce galling and seizing.
If you are interested in other Stainless Steel Channels, please click 302, 303, 304, 304L, 304H, 309, 309S, 310, 310S, 310H, 316, 316L, 317/317L, 317LMN, 321, 321H, 330, 347, 347H, 904L, 403, 405, 409, 410, 410S, 410/HT, 416, 416HT, 420, 422, 430, 440C, Duplex 2205, Duplex 2304, Duplex 2507.
Phone/whatsapp/wechat: 0086-13347910998
Add: 20-2-1705, Dongting Middle Road, Xishan District, Wuxi city, Jiangsu Province, China
E-mail: vicky@zzlsteel.com
Jiangsu Zhongzhilian Steel Industry Co., Ltd., established in 2005,is a experienced manufacturer of steel products. It is located in Wuxi, one of the biggest stainless steel bases in China. The monthly production quantity is at least 10,000 Mt.Our factory covers an area of 50，000 square meters. There are five finishing rolling production lines and two hot rolling production lines as well as advanced computer-controlled automation systems. The whole set of machines and equipment are imported from Japan and Germany which guarantee the stable quality of our products. Moreover, to meet the increasingly high standard of the market, we keep introducing ...
Read MorePhone/whatsapp/wechat: 0086-13347910998
Add: 20-2-1705, Dongting Middle Road, Xishan District, Wuxi city, Jiangsu Province, China
E-mail: vicky@zzlsteel.com